Home > News > Content

Radiant Tube The Method Of Life

Sep 28, 2017

The silicon carbide radiator is the key equipment for the continuous annealing furnace of the galvanizing unit. It is used to radiate the strip steel to eliminate the internal stress of the strip and improve the plasticity. The purpose of the annealing is to reach the purpose of annealing. However, if the leakage tube will bring the operation to the unit A certain consequence, and even affect the normal operation of production. To prevent the radiation tube is burned to extend the life of the radiation tube, take some measures. Please refer to the following description:

1, adjust the combustion gas and combustion air combustion ratio, due to the atmosphere in the nitrogen atmosphere, excessive oxygen will occur a strong nitriding oxidation, so that the radiation tube corrosion damage, so the combustion of O2 in the exhaust gas content control in less than 2%.

2, gas pressure control valve and air pressure control valve action should be sensitive, do not lag to ensure that the combustion gas pressure and air pressure stability, to ensure complete combustion of gas.

3, exhaust exhaust fan speed smooth, reduce the combustion flame fluctuations.

4, the combustion of air heat exchanger can not be leaked, to avoid the air was exhaust gas blown away, affecting the proportion of gas and air mixed combustion.

5, the heat exchanger connection flange and seal can not be leaked, to avoid the outside air into the air, as far as possible to improve the temperature of combustion air.

6, if the conditions and funding permit, you should install a large heat exchanger, the use of emissions to the plant outside the waste heat (up to 390 ℃) for the first time preheated air, air into the burner tube after the heat exchanger Second preheating the air to raise the temperature of the combustion air.

7, the radiation tube temperature> 400 ℃ (furnace temperature), is strictly prohibited to open the lid and remove the burner and heat exchanger, to avoid high temperature radiation tube cold air shrinkage caused by cracks.

8, as far as possible to arrange the same heating needs of the strip production.

9, the production as far as possible to maintain the uniformity of the working temperature, to avoid the rapid ignition of the burner and stop the burner work to carry out purge cooling operation.